Zheflon®FL2006 PVDF - Extrusion Grade | Suitable for extrusion processing of plates, bars, and pipes
Zheflon®FL2006 PVDF - Extrusion Grade | Suitable for extrusion processing of plates, bars, and pipes
Zheflon®FL2006 PVDF - Extrusion Grade | Suitable for extrusion processing of plates, bars, and pipes
Zheflon®FL2006 PVDF - Extrusion Grade | Suitable for extrusion processing of plates, bars, and pipes
Model
FL2006

Item specifics

Water Absorption(%)
≤0.15
Melt Flow Rate(g/10min)
2.0-8.0
Secondary Melting Point(℃)
165-175
Break Strength/mPa
≥25

Review

Description

Description
Zheflon®FL2006 PVDF homopolymer is medium and low viscosity grade that with high purity. 

Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of extrusion. It is suitable for the extrusion of PVDF plates, rods and pipes.
Technical Specifications
Specifications
Range
Reference Standard
Moisture Content (%)
≤0.10
GB/T 6284
Melt Flow Rate(g/10min)
2.0-8.0
Load 5kg, 230℃, GB/T 3682
Secondary Melting Point (℃)
165-175
GB/T19466
Break Strength(Thickness2.00mm)(MPa)
≥40
GB/T 1040
Elongation at Break(%)
≥10
GB/T 1040
Yield Strength(Thickness2.00mm)(MPa)
≥40
GB/T 1040
Elongation at Yield(%)
≥8
GB/T 1040
Whiteness
≥50
GB/T 2913
Yellowness
≤5
HB/T 3862